Abstract

To address the key issues of uneven distribution of functional groups, large dispersion of holographic storage performance across different regions, and poor consistency of storage capacity in traditional PQ/PMMA holographic storage photopolymers, this paper introduces a low-viscosity reactive diluent, tripropylene glycol diacrylate (TPGDA), to modify the matrix. Leveraging the viscosity-reducing and double-bond crosslinking properties of TPGDA, the molecular diffusion behavior of the system was regulated. The effects of TPGDA doping ratio, the ratio of photosensitizer PQ to thermal initiator AIBN, and post-curing process on the holographic performance uniformity of the material were systematically investigated. The uniformity was quantitatively evaluated by the variance of diffraction efficiency at different points. Visible light absorption spectra and Fourier-transform infrared (FT-IR) spectroscopy were employed to reveal the modification mechanism from the perspective of functional group distribution. Actual-data read/write tests were conducted using a collinear holographic storage system. The experimental results show that the optimal TPGDA doping concentration is 40 wt%. For the optimized formulation TPGDA:MMA:AIBN:PQ = 8 g:12 g:0.20 g:0.18 g, the modified material achieves an average diffraction efficiency of 76.58%, and the diffraction efficiency variance decreases from 23.49 (pristine matrix) to 1.64, indicating a significant improvement in performance uniformity. Compared with pure PQ/PMMA, the modified material exhibits an approximately 1.95-fold increase in maximum diffraction efficiency, a 2-fold increase in recording rate, and a 1.6–1.75-fold increase in refractive index modulation. FT-IR spectroscopy confirms that TPGDA optimizes the spatial distribution uniformity of C=C and C=O functional groups. In collinear holographic measurements, the bit error rate (BER) variance of the modified sample is reduced by 40% relative to the pristine matrix, achieving homogeneous storage performance across the entire area while maintaining comparable signal-to-noise ratio (SNR) and BER. Additional short-time UV post-curing can further enhance the diffraction efficiency and refractive index modulation, and a thinner substrate can avoid performance fluctuations caused by incomplete thermal curing of thick samples. This study achieves directional optimization of the holographic uniformity of PQ/PMMA through reactive diluent viscosity reduction modification, providing a new strategy for the formulation design and engineering preparation of high-consistency holographic storage photopolymers.

IPC Classification

Keywords