Abstract

One of the most promising absorber materials for solar applications is copper zinc tin sulfide/selenide (CZTS), which has good optical properties and basic elements that are readily available, affordable, and environmentally acceptable. This study examines how pulse timing and current density affect the electrodeposition of Cu2ZnSnS4/Cu2ZnSn(S,Se)4 (CZTS/CZTSSe) thin films from a diluted electrolyte, including deposition quality, film configuration, elemental composition, crystallinity, and photovoltaic performance. It evaluates the impact of these factors on device performance, film properties, layer’s compactness, surface homogeneity, microcrack-free morphology, compositional homogeneity, crystallinity, and suitability for solar device manufacturing. Using a pulsed-current technique, CZTS precursor layers were electrodeposited in a low-concentration solution with periodic changes in current density of roughly 5.3–5.9 mA/cm2 and pulse-on/off durations of 50/50, 100/100, and 250/250 ms. The deposited precursors were then added to fully built CZTS-based solar cell topologies after sulphurization or selenization. Structural characteristics were analyzed using X-ray diffraction (XRD), and composition and elemental distribution were assessed using energy-dispersive X-ray spectroscopy (EDS). Measurements of transmittance and reflectance were used to evaluate optical properties relevant to photovoltaic performance. In contrast to films deposited at higher current densities and longer off-times, moderate current densities combined with short off-times yield dense, microcrack-free films with improved crystallinity and near-stoichiometric Cu/(Zn + Sn), Zn/Sn, and chalcogen/metal ratios. Additionally, absorber layers with appropriate optical band gaps and improved device performance are produced by these optimized pulse parameters. Overall, the study shows that controlling pulse parameters in diluted electrolytes is a useful tactic for improving the quality of CZTS films and developing low-cost, solution-based fabrication techniques for high-performance CZTS solar cells.

IPC Classification

Keywords