Abstract

The manuscript aims to analyze the properties of gray cast iron EN GJL-250 as a function of the charge composition with an emphasis on microhardness and indentation size effect (ISE). Three compositions of cast iron were used: cast iron A as traditionally produced cast iron, B and C as inoculated and overheated cast iron micro-alloyed with FeTi70. The authors used the cutting method to assess residual stresses in castings with a stress grid designed according to Sipp. The specimens from thick and thin bars of the grid, after determination of residual stresses, were used for uniaxial tensile tests, measurement of the hardness (HBW, HV, and Vickers microhardness), metallographic, and fractographic analysis. Results of microhardness were used for the determination of ISE indices, and “true hardness” was calculated. The effect of composition has a statistically significant effect (single ANOVA; specimens from thick and thin bars are considered together) only for Meyer index n, and in the case of thick bars, also for HBW and HV.

Keywords