Abstract

The effects of ultraviolet (UV) light and moisture environments on the properties of continuous fiber-reinforced thermoplastic composites were investigated in this study. Materials included carbon fiber-reinforced polyphenylene sulfide (CF/PPS), glass fiber-reinforced polyphenylene sulfide (GF/PPS), glass fiber-reinforced polypropylene (GF/PP), and glass fiber-reinforced polyethylene terephthalate (GF/PET). Fiber orientation was noted to affect the response of the materials to UV and moisture environments. For CF/PPS, UV exposure led to enhanced unidirectional tensile and flexure properties, and quasi-isotropic compression strength, but reduced in-plane shear properties of cross-ply laminates and the short-beam shear strength of unidirectional laminates. Exposure to moisture had minimal effect on CF/PPS laminates. UV light caused a slight decrease in tensile strength and strain of unidirectional samples of GF/PPS and a slight increase in these properties with various degrees in quasi-isotropic samples. Exposure to moisture was noted to cause a reduction in most of the mechanical properties with various degrees in unidirectional and quasi-isotropic GF/PPS laminates. For GF/PP, exposure to UV and moisture decreased the tensile and compressive strengths of unidirectional and quasi-isotropic laminates. However, a notable increase in flexure strength was observed in both laminates after UV exposure. The GF/PET quasi-isotropic laminates showed reduced tension, compression, and flexure strengths but increased impact resistance and short-beam strength under UV exposure, while moisture decreased in-plane shear properties of cross-ply laminates and increased the glass transition temperature of unidirectional laminates. Vertical burn and surface flammability and smoke generation tests showed high flame resistance of CF/PPS and GF/PPS composites, and less so for GF/PP and GF/PET composites. The findings highlight the various responses of the materials to extreme environments.

IPC Classification

Keywords